Patent Amorphous Spraying and Laser or PTA Cladding Powder,Tungsten Carbide Hardmetal Clad Super Wear Plates and Tubes.  Chinese   English   Japanese

    Advanced Metallurgy Technology Co., Ltd.

    Home > Products > Hastelloy+ Hard Powder
    1. Patent Nickel Self-flux Powder NanoN for Speed Laser or PTA Cladding +Remelt of Corrosion as Hastelloy, High Abrasion, Temperature 1000℃
    2. Patent Nickel Self-flux Powder NanoN for Speed Laser or PTA Cladding +Remelt of Corrosion as Hastelloy, High Abrasion, Temperature 1000℃
    3. Patent Nickel Self-flux Powder NanoN for Speed Laser or PTA Cladding +Remelt of Corrosion as Hastelloy, High Abrasion, Temperature 1000℃
    4. Patent Nickel Self-flux Powder NanoN for Speed Laser or PTA Cladding +Remelt of Corrosion as Hastelloy, High Abrasion, Temperature 1000℃
    5. Patent Nickel Self-flux Powder NanoN for Speed Laser or PTA Cladding +Remelt of Corrosion as Hastelloy, High Abrasion, Temperature 1000℃

    Patent Nickel Self-flux Powder NanoN for Speed Laser or PTA Cladding +Remelt of Corrosion as Hastelloy, High Abrasion, Temperature 1000℃

    • Type:NanoNFH,NanoNFPTA,NanoNFL
    • Brand :AdvancedMetal
    • Sizes:15-53um,45-150um etc.

    Nickel self-fluxing alloy NanoNF and NanoN powders have similar Corrosion resist as Hastelloy C276 and Inconel625, can resist Pure Acid or Alkali corrosion and high Temperature 1000℃. NanoNF coating hardness is HV700-900 and very good Abrasion Resist. Coating crack is normal if without preheat. Preheat 250℃ or Remelt can avoid the coating cracking. Although the remelt is additional, while can benefit to the cladding at super high speed without caring cracks and take over caring the roughness from the cladding. NanoN coating hardness is HRC40-50 and good Abrasion Resist. The coating can be no cracking without preheat or remelt.

    1. Detailed information

    Patent Nickel Self-flux Powder NanoN for Speed Laser or PTA Cladding +Remelt of Corrosion as Hastelloy, High Abrasion, Temperature 1000℃

    1597246463393783.jpg

    1.Patent NanoN Nickel Powder for Speed Laser or PTA Cladding+Remelt of Corrosion as Hastelloy, High Abrasion, Temperature 1000℃ Description

    AMTmetalTech Gas Atomized Patent super Nickel self-fluxing alloy NanoNF and NanoN series powders have the similar Corrosion resistance as HastelloyC276 and Inconel625. NanoNF and NanoN can resist the Pure Acid or Alkali corrosion and the high Temperature up to 1000℃

    The NanoNF coating hardness is HV700-900 and very good Abrasion Resist. Coating crack is normal if without preheat. Preheat 250℃ or Remelt can avoid the coating cracking. Although the remelt is additional, while can benefit to the cladding at super high speed without caring cracks and take over caring the roughness from the cladding

    The NanoN coating hardness is HRC40-50 and good Abrasion Resist. The coating can be no cracking without preheat or remelt.

    NanoNFH size 15-53um is suitable for the High Speed Laser Cladding+Remelt. NanoNFL size 45-150um is for regular Laser Cladding+Remelt. NanoNFPTA size 45-150um is for PTA Plasma Cladding+Remelt.

     Type

     Chemical Composition(%)

    NanoNFH, 

    NanoNFL, 

    NanoNFPTA, 

    NanoNL, 

    NanoNPTA

     

    Ni

     

    Cr

     

    Cu

     

    Co

    Nb+ Ti

     

    Si

     

    Mo

     

    B

     

    P

     

    Mn

     

    Fe

     

    C

     

    Zr

    Ce+ La

    Balance

     

    15-

    45

     

    0.00

    1-15

     

    0.00

    1-10

     

    0.00

    1-10

    0.0

    1-

    12

     

    0.00

    1-10

    0.0

    01-

    6

    0.0

    01-

    8

    0.0

    01-

    5

    0.0

    1-

    15

     

    ≤ 0.3

     

    0.0

    7-3

     

    0.01

    1-1

    NanoNL size 45-150um is for regular Laser Cladding. NanoNPTA size 45-150um is for PTA Plasma Cladding.

    PTA Plasma swing cladding can achieve fine coating thickness down to 0.4mm.

    2.Patent NanoN Nickel Powder for Speed Laser or PTA Cladding+Remelt of Corrosion as Hastelloy, High Abrasion, Temperature 1000℃ Applications

    AMTmetalTech Patent Nickel self-fluxing Alloy Powder NanoNF and NanoN are suitable for the Severe Corrosion as Hastelloy, High Abrasion and High Temperature 1000℃ Resist by High Speed Laser Cladding+Remelt Cylinders, Drive Pipes, Pulp Rolls, Pistons, or Regular Laser Cladding Spectacle Pipes and Glass Molds, or PTA Plasma Swing Cladding+Remelt replacing Chrome Plating and Long Tube Inside Coating etc.

    1597246506416762.jpg

    3. Patent NanoN Nickel Powder for Speed Laser or PTA Cladding+Remelt of Corrosion as Hastelloy, High Abrasion, Temperature 1000℃ Packagings

    The standard packaging is by plastic bottle per 5kg. We can do the other packaging according to the customer requirements. 


    Please send your inquiry to us by email about our Patent Amorphous HVAF or HVOF Spraying Powders including for tube or pipe inside coating, Patent Nickel Alloy powder more wear resist than Hastelloy and Inconel of severe corrosion, high temperature and abrasion resist for high speed Laser Deposit and PTA welding cladding and Plasma surfacing or overlay, Tungsten Carbide Hardmetal Cemented Quick Assembly Clad Mud Pump Liner and Wear Plates for Crushing / Excavator / Auger tips / Brick Mold or Mould, PDC Cutter Diffusion Bonding, PDC Diamond Bearing and Brazing etc.